Investigation on thermal conductivity and mechanical properties of Si3N4 ceramics via one-step sintering

High thermal conductivity Si₃N₄ ceramics were fabricated using a one-step method consisting of reaction-bonded Si₃N₄ (RBSN) and post-sintering. The influence of Si content on nitridation rate, β/(α+β) phase rate, thermal conductivity and mechanical properties was investigated in this work. It is of special interest to note that the thermal conductivity showed a tendency to increase first and then decrease with increasing Si content. This experimental result shows that the optimal thermal conductivity and fracture toughness were obtained to be 66 W (m K)^-1 and 12.0 MPa m^1/2, respectively. As a comparison, the nitridation rate and β/(α+β) phase rate in a static pressure nitriding system, i.e., 97% (MS10), 97% (MS15), 97% (MS20) and 8.3% (MS10), 8.3% (MS15), 8.9% (MS20), respectively, have obvious advantages over those in a flowing nitriding system, i.e., 91% (MS10), 91% (MS15), 93% (MS20) and 3.1% (MS10), 3.3% (MS15), 3.3% (MS20), respectively. Moreover, high lattice integrity of the β-Si₃N₄ phase was observed, which can effectively confine O atoms into the β-Si₃N₄ lattice using MgO as a sintering additive. This result indicates that one-step sintering can provide a new route to prepare Si₃N₄ ceramics with a good combination of thermal conductivity and mechanical properties.     

High-temperature stabilization of polypropylene using hindered phenol–thioester stabilizer combinations,Part 1: Optimization and efficacy via nondust blends

The thermal degradation of unstabilized polypropylene has been investigated under long-term processing (twin extruder) and thermal aging at 150°C, with additive concentration studies on combinations of an established hindered phenolic antioxidant (pentaerythritol tetrakis (3-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate) [S1010] and two popular thioesters (distearyl-3,3′-thiodipropionate [DSTDP] and didodecyl-3,3′-thiodipropionate [DLTDP]) using melt flow rate, carbonyl index and powder diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) (FTIR), and differential scanning calorimetry (DSC) (oxidation induction time [OIT]) and ultimate embrittlement time (Fracture) on injection-molded test pieces. It was found that 20:80 phenol:thioester ratios provided the best long-term thermal stability (LTTS); however, this was the reverse for processing stabilization (80:20), underlining the antioxidant nature of the two stabilizers (long term vs. melt). Melt preblending of the stabilizers (to form a no-dust blend) gave rise to improved LTTS. DRIFTS FTIR indicated that there was an improvement in preblending the additives, which removed any volatile impurities. Increased additive dispersion and localized potential efficacy in the stabilization cycle is important, as well as possible improved addition of the additives to the extruder rather than fine powder. The data are discussed in relation to the long-term stabilization of polypropylene in high-temperature applications such as under the bonnet of automobiles where minimizing stabilizer losses and maximizing synergy are important.     

Dual-phase rare-earth-zirconate high-entropy ceramics with glass-like thermal conductivity

A series of rare earth zirconates (RE₂Zr₂O₇) high-entropy ceramics with single- and dual-phase structure were prepared. Compared with La₂Zr₂O₇ and Yb₂Zr₂O₇, the smaller “rattling” ions (Yb³⁺, Er³⁺, Y³⁺) have been incorporated into pyrochlore lattice in (La_0.2Nd_0.2Y_0.2Er_0.2Yb_0.2)₂Zr₂O₇ (LNYEY) while larger ions (La³⁺, Nd³⁺, Sm³⁺, Eu³⁺) incorporated into fluorite lattice in (La_0.2Nd_0.2Sm_0.2Gd_0.2Yb_0.2)₂Zr₂O₇ (LNSGY). Due to high-entropy lattice distortion and resonant scattering derived from smaller ions Yb³⁺, Er³⁺, and Y³⁺, LNYEY shows a lower glass-like thermal conductivity (1.62-1.59 W m^-1 K^-1, 100-600℃) than LNSGY (1.74-1.75 W m^-1 K^-1, 100-600℃). Moreover, LNYEY and LNSGY exhibit enhanced Vickers’ hardness (LNYEY, H_v = 11.47 ± 0.41 GPa; LNSGY, H_v = 10.96 ± 0.26 GPa) and thermal expansion coefficients (LNYEY, 10.45 × 10^-6 K^-1, 1000℃; LNSGY, 11.02 × 10^-6 K^-1, 1000℃). These results indicate that dual-phase rare-earth-zirconate high-entropy ceramics could be desirable for thermal barrier coatings.     

油页岩干酪根热解产物特性研究

采用裂解色谱（PY-GC-MS）、电子顺磁共振波谱（EPR）和红外光谱（FTIR）等技术手段，分析了Estonia油页岩中干酪根及其热解产物的结构特性，研究了不同温度下中间产物与最终产物的关联性。结果显示：油页岩热解符合干酪根热解为中间产物热沥青，热沥青再热解为页岩油、干馏气和半焦等产物反应路径，中间产物热沥青的生成趋势反映了终产物的生成速率变化；H₂、CH₄和C₂~C₅组分主要来自热沥青中脂肪烃的芳构化、芳香族化合物烷基侧链的断裂及含氧化合物的缩聚等，干酪根热解产生的烷烃和烯烃类化合物是产油气的主要组分。干酪根和页岩油的自由基自旋浓度明显低于热沥青和半焦；半焦g值最大，干酪根次之，热沥青和页岩油的g值偏低。     

Nitrate Additives Coordinated with Crown Ether Stabilize Lithium Metal Anodes in Carbonate Electrolyte

Lithium metal anodes (LMAs) are promising for next-generation batteries but have poor compatibility with the widely used carbonate-based electrolytes, which is a major reason for their severe dendrite growth and low Coulombic efficiency (CE). A nitrate additive to the electrolyte is an effective solution, but its low solubility in carbonates is a problem that can be solved using a crown ether, as reported. A rubidium nitrate additive coordinated with 18-crown-6 crown ether stabilizes the LMA in a carbonate electrolyte. The coordination promotes the dissolution of NO₃⁻ ions and helps form a dense solid electrolyte interface that is Li₃N-rich which guides uniform Li deposition. In addition, the Rb (18-crown-6)⁺ complexes are adsorbed on the dendrite tips, shielding them from Li deposition on the dendrite tips. A high CE of 97.1% is achieved with a capacity of 1 mAh cm⁻² in a half cell, much higher than when using the additive-free electrolyte (92.2%). Such an additive is very compatible with a nickel-rich ternary cathode at a high voltage, and the assembled full battery with a cathode material loading up to 10 mg cm⁻² shows an average CE of 99.8% over 200 cycles, indicating a potential for practical use.     

“高电压技术”课程线上线下混合式教学

本文采用超星学习通线上教学平台，以 “高电压技术”课程为对象，实施了规模为120余人的线上线下混合式教学。基于线上教学和传统教学的优势互补，设计了“高电压技术”多个教学环节。归纳分析了混合式教学在各个教学环节取得的效果和问题，并根据学生反馈提出了持续性的改进措施。     

Toward a better understanding of multifunctional cement-based materials: The impact of graphite nanoplatelets (GNPs)

The impact of graphite nanoplatelets (GNPs) on the physical and mechanical properties of cementitious nanocomposites was investigated. A market-available premixed mortar was modified with 0.01% by weight of cement of commercial GNPs characterized by two distinctively different aspect ratios.The rheological behavior of the GNP-modified fresh admixtures was thoroughly evaluated. Hardened cementitious nanocomposites were investigated in terms of density, microstructure (Scanning Electron Microscopy, SEM and micro–Computed Tomography, μ-CT), mechanical properties (three-point bending and compression tests), and physical properties (electrochemical impedance spectroscopy, EIS and thermal conductivity measurements). At 28 days, all GNP-modified mortars showed about 12% increased density. Mortars reinforced with high aspect ratio GNPs exhibited the highest compressive and flexural strength: about 14% and 4% improvements compared to control sample, respectively. Conversely, low aspect ratio GNPs led to cementitious nanocomposites characterized by 36% decreased electrical resistivity combined with 60% increased thermal conductivity with respect to the control sample.     

Research advances in residual thermal stress of ceramic/metal brazes

Brazing, as a common method of bonding ceramic and metal, has been applied in microelectronics, aerospace, machinery and other domains extensively. The residual thermal stress in the brazed joint has direct effects on the mechanical properties of the joint, so how to control the generation of residual thermal stress has become the vital point. In this paper, the methods of reducing residual thermal stress in the brazing process in recent years are reviewed. The generation and effects of residual thermal stress in the brazed joint are introduced. Besides, the methods of detecting residual thermal stress are discussed, and different methods of reducing residual thermal stress in brazed joints are also analyzed. Finally, the future development directions of reducing residual thermal stress in the brazed joint are proposed.     

Thermal and dynamic mechanical behavior of epoxy composites reinforced with post-consumed yerba mate

Yerba mate (YM) is widely consumed in Latin American countries, and its residues can be used as bio-resources such as reinforced in epoxy composites. The present work aims to produce epoxy resin composites and evaluate the influence of post-consumed YM as reinforcement. The concentrations of YM used were 5, 10, and 20% (wt/wt). Chemical, thermal, morphological, and dynamic mechanical behaviors were explored. The YM incorporation did not influence chemically on the epoxy structure and a pull-out phenomenon was observed as YM content increased. The YM at lower concentrations (5 and 10%) led to higher values of activation energies calculated from model-free isoconversional methods. On the other hand, the composite e/YM 20 wt% improved all dynamic-mechanical properties. YM proved to be a suitable and cheap reinforcement for epoxy resin.